[1]马军翔,潘小鹏,沈濂,等.水性聚氨酯性能评估及其仿皮着色涂层应用[J].现代纺织技术,2020,28(4):71-77.
 MA Junxiang,PAN Xiaopeng,SHEN Lian,et al.Evaluation and Application of Waterborne Polyurethanefor Imitationleather Colored Coating[J].Advanced Textile Technology,2020,28(4):71-77.
点击复制

水性聚氨酯性能评估及其仿皮着色涂层应用()
分享到:

《现代纺织技术》[ISSN:1009-265X/CN:33-1249/TS]

卷:
28
期数:
2020年4期
页码:
71-77
栏目:
出版日期:
2020-07-10

文章信息/Info

Title:
Evaluation and Application of Waterborne Polyurethanefor Imitationleather Colored Coating
文章编号:
1009-265X(2020)04-0071-07
作者:
马军翔潘小鹏沈濂李栋黄益郑今欢
1.先进纺织材料与制备技术教育部重点实验室,杭州310018;2.浙江省清洁染整技术研究重点实验室,浙江绍兴312000;3.浙江皮意纺织有限公司,浙江海宁314400
Author(s):
MA Junxiang PAN Xiaopeng SHEN LianLI Dong HUANG Yi ZHENG Jinhuan
1.Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education,Hangzhou 310018, China; 2.Key Laboratory of Clean Dyeing and Finishing Technology of ZhejiangProvince, Shaoxing 312000, China; 3.Zhejiang PiYi Textile Co., Ltd, Haining 314400, China
关键词:
仿皮涂层水性聚氨酯物理机械性能摩擦色牢度
分类号:
TS195.645
文献标志码:
A
摘要:
为解决溶剂型聚氨酯仿皮涂层加工中有机溶剂挥发对环境及人员健康的危害,开发环保型水性聚氨酯仿皮涂层剂以取代溶剂型产品。从水性聚氨酯树脂优选,水性聚氨酯固化膜拉伸物理机械性能,水性聚氨酯涂层剂消泡性能及水性聚氨酯着色涂层加工工艺等方面进行了研究。结果表明:当涂层配方为质量分数97%水性聚氨酯PUE1401、1%着色剂颜料、0.5%消泡剂AFCONA 2502、1% SA海藻酸钠;涂层加工条件为固化温度150 ℃、固化时间3 min,所制备的水性聚氨酯仿皮着色涂层面料耐干、湿摩擦色牢度分别可达3~4级和3级,且涂层表面手感柔软爽滑。上述研究结果可为企业开发水性聚氨酯仿皮着色涂层产品提供理论支持和技术方案。

参考文献/References:

[1] 任龙芳,赵国徽,强涛涛,等.超细纤维合成革仿天然皮革研究进展[J].皮革科学与工程,2012(1):38-42.
[2] XU X, WU Z P. Environmental cost analysis and upgrading research of synthetic leather industry[J]. Energy Procedia, 2011,5:1341-1347.
[3] 〖JP2〗WU Y T, WEN S G, CHEN K M, et al. Enhanced corrosion resistance of waterborne polyurethane containing sulfonated graphene/zinc phosphate composites[J]. Progress in Organic Coatings, 2019,132:409-416.
[4] LIU Z M, WU B, JIANG Y, et al. Solventfree and selfcatalysis synthesis and properties of waterborne polyurethane[J]. Polymer, 2018,143:129-136.
[5] 吴一帆,赵海鹏.国内水性聚氨酯研究进展[J].中外能源,2018,23(5):69-77.
[6] WANG X, XING W Y, FENG X M, et al. Enhanced mechanical and barrier properties of polyurethane nanocomposite films with randomly distributed molybdenum disulfide nanosheets[J]. Composites Science & Technology, 2016,127:142-148.
[7] 张悦.一种纯棉功能性仿皮革面料的涂层制备方法[J].皮革与化工,2017(4):20-23.
[8] 任龙芳,耿瑾,邢政国,等.混合异氰酸酯型聚氨酯的制备与耐黄变性能[J].精细化工,2018,35(3):504-510.
[9] 刘清华,邢鹏程.水性涂料用着色剂的选择[J].涂料工业,2018(8):31-37.
[10] NIEMCZYK A, PIEGAT A, SOMSECA OLALLA , et al. New approach to evaluate microphase separation in segmented polyurethanes containing carbonate macrodiol[J]. European Polymer Journal, 2017,93:182-191.

备注/Memo

备注/Memo:
收稿日期:2019-06-21
网络出版日期:2019-11-26
基金项目:浙江省基础公益研究计划项目(LGG18E030008);先进纺织材料与制备技术教育部重点实验室(浙江理工大学)开放基金项目(2017QN03);浙江省清洁染整技术研究重点实验室开放基金项目(NO.1806)
作者简介:马军翔(1996-),男,安徽肥西人,硕士研究生,主要从事光固化涂层方面的研究
通信作者:黄益,E-mail:yihuang@zstu.edu.cn
更新日期/Last Update: 2020-07-02