|本期目录/Table of Contents|

[1]易玲敏,叶星星.不同温度下酸催化有机硅单体开环共聚制备含氢硅油的研究[J].现代纺织技术,2017,25(02):50-53.
 ZHOU Hong,YI Lingmin,YE Xingxing.Study on Preparation of Hydrogen Containing Silicone Oil byRing Opening Copolymerization of Organsilicone MonomerSubject to Acid Catalysis under Different Temperature[J].Advanced Textile Technology,2017,25(02):50-53.
点击复制

不同温度下酸催化有机硅单体开环共聚制备含氢硅油的研究()
分享到:

《现代纺织技术》[ISSN:1009-265X/CN:33-1249/TS]

卷:
25
期数:
2017年02期
页码:
50-53
栏目:
出版日期:
2017-03-10

文章信息/Info

Title:
Study on Preparation of Hydrogen Containing Silicone Oil byRing Opening Copolymerization of Organsilicone MonomerSubject to Acid Catalysis under Different Temperature
文章编号:
1009-265X(2017)02-0050-04
作者:
易玲敏叶星星
浙江理工大学,a.先进纺织材料与制备技术教育部重点实验室;b.生态染整技术教育部工程研究中心,杭州310018
Author(s):
ZHOU Hong YI Lingmin YE Xingxing
a.Key Laboratory of Advanced Textile Materials & Manufacturing Technology, Ministry of Education; b.Engineering Research Center for EcoDyeing & Finishing of Textiles,Ministry of Education, Zhejiang SciTech University, Hangzhou 310018, China
关键词:
有机硅单体酸催化开环聚合含氢硅油
分类号:
TQ264.1
文献标志码:
A
摘要:
以98%浓硫酸为催化剂,进行了八甲基环四硅氧烷(D-4)与四甲基环四硅氧烷(D-H-4)的阳离子开环共聚并得到含氢硅油,重点考察了不同共聚温度对聚合产物转化率、含氢值及其分子量分布的影响。研究结果表明:在温度30 ℃条件下,制备得到的聚合物分子量和含氢值接近理论值,增加共聚温度对聚合物转化率的提高帮助不大,且会使聚合物的分子量分布变宽。

参考文献/References:

[1] IZMAILOV B A, NEDELKIN A V, RODLOVSKAYA E N, et al. Molecular assembly of nanolayers of waterrepellent siloxane coatings on the surface of fibers[J]. Fibre Chemistry, 2012,43(6):433-435.
[2] ZHAO X, ZHU W Y. The synthesis characterization and application of aminomodified polymethylhydrosiloxane softener[C]//Wang Rui , liu Huawu. Advanced Materials Research. Switzerland: Trans Tech Publications Ltd, 2011,331:390-393.
[3] ZHOU Y. The research on the application of super soft aminomodified silicone oil SM20 for PET fabrics[C]//Bai Lun, Chen Guoqiang. Advanced Materials Research. Switzerland: Trans Tech Publications Ltd, 2011,175:677-680.
[4] CHENG J, LI M, CAO Y, et al. Synthesis and properties of photopolymerizablebifunctional polyethermodified polysiloxane polyurethane acrylate prepolymer[J]. Journal of Adhesion Science and Technology, 2015,30(1):2-12.[5] ZHOU Y Q, ZHENG C, ZHAN Y, et al. The performance of polyether modified polysiloxane[C]//Chen Shuang, Liu Zhaotie, Zeng Qingzhu. Advanced Materials Research. Switzerland: Trans Tech Publications Ltd, 2012,554:140-146.
[6] XIONG B, ZHU S, FAN Y, et al. Hydrophobic modification of poly(ethylene terephthalate) with epoxymodified polysiloxane by reactive extrusion[J]. Journal of Macromolecular Science, Part B, 2012,51(4):630-641.
[7] LINDNER T, GEISBERGER G, PACHALY B. Process for preparing methylhydrogenpolysioxanes having trimethylsilyl end groups: US, 6143912[P].2000A11-07.
[8] 来国桥,幸松民.有机硅产品合成工艺及应用[M].北京:化学工业出版社,2010:382.
[9] 吕起,余金全,刘登政.一种甲基含氢硅油的生产方法:CN,102408566[P].2010-04-11.
[10] 李坤,易玲敏,孟晓美,等.含氟硅氧烷改性有机硅聚合物对蚕丝织物的表面改性研究[J].丝绸,2013,50(3):1-5.
[11] 商春燕,袁慎峰,尹红,等.1H NMR测定含氢硅油含氢量及分子量[J].光谱实验室,2011,28(3):1287-1292.

备注/Memo

备注/Memo:
收稿日期:2016-02-26
作者简介:周鸿(1990-),男,安徽铜陵人,硕士研究生,主要从事为特殊浸润性纤维/织物表面的构建与结构性能调控
通信作者:易玲敏,E-mail:lmyi@zstu.edu.cn
更新日期/Last Update: 2017-03-20