 MD Ali Hossain,CHEN Weiguo,WANG Chenglong,et al.Effect of Oxygen Plasma Processing on Digital Transfer Printing of Polyester Fabric[J].Advanced Textile Technology,2020,28(2):70-75.
点击复制

氧等离子体处理对涤纶织物数码转移印花的作用()
分享到:

《现代纺织技术》[ISSN:1009-265X/CN:33-1249/TS]

卷:
28
期数:
2020年2期
页码:
70-75
栏目:
出版日期:
2020-03-10

文章信息/Info

Title:
Effect of Oxygen Plasma Processing on Digital Transfer Printing of Polyester Fabric
文章编号:
1009-265X(2020)02-0070-06
作者:
MD Ali Hossain陈维国王成龙金淑兰吴浩张亚
 1.浙江理工大学生态染整技术教育部工程研究中心,杭州310018;2.金华洁灵家居用品有限公司,浙江金华321037
Author(s):
MD Ali Hossain CHEN Weiguo WANG ChenglongJIN Shulan WU Hao ZHANG Ya
1.Engineering Research Center for EcoDyeing & Finishing of Textiles, Ministry of Education,Zhejiang Sci-Tech University,Hangzhou 310018, China; 2.Jinhua JielingHousehold Goods Co., Ltd., Jinhua 321037, China
关键词:
等离子体数码转移印花涤纶织物表面改性表面粗糙度
分类号:
TS190.8
文献标志码:
A
摘要:
为了研究低温等离子体处理对涤纶织物数码转移印花的影响,采用扫描电子显微镜(SEM)观察,发现了经等离子体处理的涤纶纤维表面被明显刻蚀,使纤维表面产生大量的细微凹孔;通过X光电子能谱(XPS)分析,揭示了经等离子体处理的涤纶纤维表面含氧化学基团有所增加;同时,接触角测试表明等离子体处理的涤纶织物润湿性有了明显的提升。显然,氧等离子体中高能粒子的撞击导致涤纶纤维表面大分子链发生部分降解,表现为处理后涤纶纤维表面粗糙度的提高,使得纤维比表面积提高,增加了热转移印花中分散染料在纤维表面的富集和染着,而纤维表面粗糙度的增加也改变了纤维表面的光反射特征,进而又促进了涤纶织物转移印花得色率的提高。热重分析(TG)表明等离子体对涤纶织物造成的损伤非常小,甚至低于热转移过程本身造成对纤维的损伤。所以,等离子体处理可以作为涤纶织物数码转移印花的前处理,以减少分散染料墨水的消耗。

参考文献/References:

[1] DAWSON T L, HAWKYARD C J. A new millennium of textile printing[J]. Coloration Technology, 2010,30(1):7-20.
[2] CONSTERDINE K. Heat transfer printing[J]. Coloration Technology, 2010,7(1):34-42.
[3] GASHTI M P, WILLOUGHBY J, AGRAWAL P. Surface and bulk modification of synthetic textiles to improve dyeability[J]. Textile Dyeing,2011(12):261-298.
[4] NATARAJAN S, MOSES J J. Surface modification of polyester fabric using polyvinyl alcohol in alkaline medium[J]. Indian Journal of Fibre & Textile Research. 2012,37(3):287-291.
[5] ZERONIAN S H, COLLINS M J. Surface modification of polyester by alkaline treatments[J]. Textile Progress, 1989,20(2):1-26.
[6] CAMMARANO A, LUCA G D, AMENDOLA E. Surface modification and adhesion improvement of polyester films[J]. Central European Journal of Chemistry, 2013,11(1):35-45.
[7] ZILLE A, OLIVEIRA F R, SOUTO A P. Plasma treatment in textile industry[J]. Plasma Processes and Polymers,2015,12(2):98-131.
[8] KAN CW, YUEN CWM, TSOI WY. Using atmospheric pressure plasma for enhancing the deposition of printing paste on cotton fabric for digital inkjet printing[J]. Cellulose. 2011,18(3):827-39.
[9] RAFFAELEADDAMO A, SELLI E, BARNI R, et al. Cold plasmainduced modification of the dyeing properties of poly(ethylene terephthalate) fibers[J]. Applied Surface Science, 2006,252(6):2265-2275.
[10] PRANSILP P, PRUETTIPHAP M, BHANTHUMNAVIN  W, et al. Surface modification of cotton fabrics by gas plasmas for color strength and adhesion by inkjet ink printing[J]. Applied Surface Science, 2016,364:208-220.

相似文献/References:

[1]张珊艳. 高能辐射接枝在纺织品改性方面的研究进展[J].现代纺织技术,2012,(05):56.
 ZHANG Shanyan. Progress of Researches on Radiation Grafting Technology in Textile Modification[J].Advanced Textile Technology,2012,(2):56.

备注/Memo

备注/Memo:
收稿日期:2018-12-14
网络出版日期:2019-03-19
作者简介:MD Ali Hossain(1992-),男,孟加拉国,硕士研究生,主要从事数码印花前处理技术方面的研究
通信作者:陈维国,E-mail:wgchen_62@126.com
更新日期/Last Update: 2020-04-06